HIGH CARBON STEEL GRIT.
Our Products
Cast Steel Grit is produced by crushing of specific sizes of steel shot. Two out of three product range is heat treated. It is utilized for blast cleaning as well as surface preparation job by the industry.
Â
GP STEEL GRIT
Quenched & tempered product, used in wheel blast machine for the faster cleaning of product. Product has same hardness of Steel Shot which is 46~51 HRC. Initially shape is angular & during operation shape changes to round. Suitable for Desanding / descaling applications.
GP STEEL GRIT
Quenched & tempered product, used in wheel blast machine for the faster cleaning of product. Product has same hardness of Steel Shot which is 46~51 HRC. Initially shape is angular & during operation shape changes to round. Suitable for Desanding / descaling applications.
GH STEEL GRIT
This is product is untampered, has highest hardness >60 HRC. Recommended to use only in Air Blasting Machines or Stone Cutting applications. Product shape always use to be angular. During operation particles break & form smaller size with angular only. This product is particularly effective in surface treatment and produce a uniform, etched finish.
Gallery
| Sreen No | 7 | 8 | 10 | 12 | 14 | 16 | 18 | 20 | 25 | 30 | 35 | 40 | 45 | 50 | 80 |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
Screen No |
2.80 |
2.36 |
2.00 |
1.70 |
1.40 |
1.18 |
1.00 |
0.85 |
0.71 |
0.60 |
0.50 |
0.42 |
0.35 |
0.30 |
0.18 |
|
G12 |
TP |
12 Max |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
G14 |
|
TP |
10 MAX |
|
|
|
|
|
|
|
|
|
|
|
|
|
G16 |
|
|
TP |
10 MAX |
|
80 MIN |
90 MIN |
|
|
|
|
|
|
|
|
|
G25 |
|
|
|
TP |
40 MAX |
|
|
|
85 MIN |
97 MIN |
|
|
|
|
|
|
G40 |
|
|
|
|
|
TP |
20 MAX |
|
|
85 MIN |
97 MIN |
|
|
|
|
|
G50 |
|
|
|
|
|
|
|
TP |
10 MAX |
|
|
|
80 MIN |
90 MIN |
|
|
G80 |
|
|
|
|
|
|
|
|
|
TP |
20 MAX |
|
|
75MAX |
|
|
G120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
TP |
10 MAX |
Chemical Composition
| Elements | Specification |
|---|---|
|
Carbon |
0.8-1.2% |
|
Silicon |
0.4-1.2% |
|
Managnese |
0.6-1.2% |
|
Sulphur |
0.05%Max |
|
Phosphorous |
0.05% Max |
- Density: 7.6 gm/cc
- Microstructure: Tempered Martensite
- Hardness:GP47~52 HRC, GL – 53~57 HRC, GH – 60 HRC+
- Durability: GP-2600~2900 cycles, GL – 2000~2500 cycles, GH – 1200~1500 cycles